ZrO2 Zirconia Ceramic Balls |
Si3N4 Silicon Nitride Ceramic Balls |
SiC Silicon Carbide Balls |
Al2O3 Aluminum Oxide Ceramic Balls |
| Material |
Zro2 |
Si3N4 |
SiC Silicon Carbide |
Al2O3 Aluminum Oxide |
| Specifications |
φ0.1mm-φ63.5mm |
φ0.4mm-φ100mm |
φ0.5mm-φ50mm |
Ceramic grinding media |
| Hardness |
HRC70-HRC73,HV:1100-1300 |
HRC75-80,HV:1300-1600 |
HRC85-90 HV: above 2100 |
>92 Al2O3 |
| Density |
6g/cm3 |
3.2g/cm3 |
3.1g/cm3 |
>3.60 |
| Performance |
1. High strength and high toughness, no broken beads under high-speed impact. |
1.59% lighter than steel balls, which means less centrifugal force and wears less grooves at high speeds and accelerations |
Silicon carbide ceramic balls have stable performance, and silicon nitride has good overall performance. Compared with steel, its |
1. High wear-resisting: The alumina balls wear resisting is higher than the common ceramic balls. When it is working, the ball |
| 2. Good sphericity and smooth surface. |
2. The elastic modulus is 44% larger, which means less deformation under load. |
mass is lighter than steel, its friction coefficient is smaller, its motion performance is better, its elastic modulus is 50% |
will not pollute the grinded materials, so it can keep the purity and improve the stability of grinded materials especially the |
| 3. Ultra-low wear, wear resistance is 30-50 times that of glass beads, 5 times that of zirconium silicate beads, and 6-8 times |
3. Smaller friction coefficient. |
larger than that of steel, its thermal expansion coefficient is smaller than 25% of that of steel, it can maintain high strength |
ceramic glaze. |
| that of alumina beads. |
4. The linear expansion coefficient of silicon nitride ceramic ball is 3.2×10-6/K, which is almost 1/4 of bearing steel, and can |
and hardness before 1000ºC under high temperature, and it is resistant to corrosion. No rust, non-magnetic, can work without oil |
2. High density: the high density, high hardness and the high grinding Characters save the grinding time, enlarge the smashing |
| 4. High density and high grinding efficiency. |
endure high temperature. |
lubrication. |
room. So It can improve the grinding efficiency. |
| |
5.Excellent surface finish can be achieved, Ra can be 4~6. |
|
|
| |
6. Can endure high temperature, high hardness and strength up to 1050 ºC. |
|
|
| Application |
Special bearings, pumps and valves that operate in aggressive environments, check valves, flow meters, measurement instruments. |
Special bearings, high-speed bearings, under vacuum pumps, compressors, centrifugal pumps, shafts/mandril, recirculating balls, |
Including Special bearings and pumps, electric switches and sensors, medical instruments. They are used in automotive, aviation |
Ceramics, cements, paints, refractory, inorganic mineral powders and other materials to form. Special bearings, check valves, |
| They are used in the medical field (very pure material). Grinding and milling applications. |
flow meters, measurement instruments. They are used in aerospace. |
and aerospace, naval, petroleum, chemical and electronic industry. Spray nozzles, shot blast nozzles and cyclone components. |
pumps and valves that operate in aggressive environments, petroleum pumps, flow meters, measurement instruments, medical devices. |
| Packing |
Standard: 10kg or 20kg per carton, 1 ton per pallet or as customer required |
OPP bag, Vacuum packing, Carton, drum, wooden case with foam; Custom packing |
OPP bag, Vacuum bag, Custom packaging |
| Delivery time |
Stock within a short time or 35 days. |
Audited Supplier 
){kind=link}
){kind=link}